410S roostevabast terasest mähis
Kirjeldus
Tehnilised andmed:
1. Standard: ASTM A240, JIS G4304, EN10088
2. Hinne: 200-seeria ja 300-seeria ja 400-seeria
3. Paksus: 0,03mm - 6,0mm
4. Laius: 8mm-600mm
5. Pikkus: vastavalt klientide soovile
6. Pind: 2D, 2B, BA, peegli viimistletud, N04, juuksejoon, matt viimistlus, 6K, 8K
7.Tehnoloogia: külmtõmmatud/külmvaltsitud/kuumvaltsitud
Materjalid:
| Tüüp | Hinne | Hinne | Keemiline komponent % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | muud | |||
| Austeniitne | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5.50–7.50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1.00 | - | ≤0,25 | － | ||
| 301 | 1,4310 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304L | 1,4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1,4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1,4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1,4550 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| 347H | 1.494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| Dupleks | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2.00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1.00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0.5 | 0,24-0,32 | ||
| Ferriit | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1.00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1.00 | - | 0,035 | Ti+Nb: 0,2+4(C+N)~0,80 | |
| Martensiit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Põhiandmed
410s roostevabast terasest mähis, hea korrosioonikindluse ja töödeldavusega, on üldotstarbeline teras ja lõikeriistade teras.410S on terase liik, mis võib parandada 410 terase korrosioonikindlust ja vormitavust. 410S on ülitugev teras, mis võib veelgi parandada 410 terase korrosioonikindlust.Seda kasutatakse turbiini labade ja kõrge temperatuuriga osade jaoks.
• Tehnilised andmed: AISI 410s, ASTM 410s
• Viimistlused: Ba pind, 2b pind, nr 1 (valge nahk), 2D pind, nr 4 (jäätunud), HL (traadi tõmbamine), 8K pind on suurepärase pinnakvaliteediga
• Kehtivad freesi paksuse ja tasasuse tolerantsid. Kui vajate konkreetseid suurusi või tera suunda, helistage JM Steelile.
410S Iseloomulik töötlemistehnoloogia
1D – pinnal on katkendlik teraline kuju, tuntud ka kui udupind.
Töötlemistehnoloogia: kuumvaltsimine + lõõmutamine haavelpeening marineerimine + külmvaltsimine + lõõmutav peitsimine.
2D – kergelt hõbedane valge värv.
Töötlemistehnoloogia: kuumvaltsimine + lõõmutamine haavelpeening marineerimine + külmvaltsimine + lõõmutav peitsimine.
2B – hõbevalge, parema läike ja tasapinnaga kui 2D-pind.
Töötlemistehnoloogia: kuumvaltsimine + lõõmutamine haavel-peening marineerimine + külmvaltsimine + lõõmutamine peitsimine + karastamine ja karastamine valtsimine.
Ba - Suurepärane pinnaläige, kõrge peegeldusvõime, nagu peegelpind.
Töötlemistehnoloogia: kuumvaltsimine + lõõmutamine haavelpeening peitsimine + külmvaltsimine + lõõmutamine peitsimine + pinna poleerimine + karastamine ja karastusvaltsimine.
Nr.3 -- Hea läikega, jämedateraline pind.
Töötlemistehnoloogia: poleerimine ja karastusvaltsimine 2D või 2B jaoks 100-120 abrasiivse materjaliga (JIS R6002).
Nr.4 -- Hea läige, peened jooned pinnal.
Töötlemisprotsess: 2D või 2B poleerimine ja karastamine 150–180 abrasiivse materjaliga (JIS R6002).
HL -- Hõbehall juuksetriipudega.
Töötlemistehnoloogia: 2D-tooted või 2B-tooted, millel on pinna poleerimiseks sobiva abrasiivmaterjali granulaarsus, on pidev abrasiivtera.
MIRRO -- Spekulaarne.
Töötlemistehnoloogia: 2D-tooted või 2B-tooted, mille lihvimismaterjali granulaarsus on peegliefekti lihvimine ja poleerimine.